ABSTRACT: This paper concerns on the influence of Ti contents on the properties of nc-TiC/a-C nanocomposite coatings deposited via co-sputtering of Ti and graphite targets. Advanced characterization techniques such as XRD, XPS, TEM, nanoindenter etc. were employed to determine the structures and properties of the coatings. Experimental results indicated that at low Ti compositions of less than 8 at.%, Ti exists in the coatings as an amorphous phase. From 8 to 45 at.%Ti, the formations of nanocomposite were confirmed. Higher than that, the coatings were almost crystalline TiC.   Nanocomposite may have a hardness comparable to that of DLC (about 33 GPa) but the residual stress is much lower. Such new nanocomposite show great potentials for engineering applications.
Toàn văn bài báo ( Thầy/cô vui lòng đăng nhập bằng email ...@hcmute.edu.vn để xem)
Góp ý
Họ và tên: *  
Email: *  
Tiêu đề: *  
Mã xác nhận:
 
 
   
  
 
 
   
 *
Copyright © Tạp Chí Khoa Học Giáo Dục Kỹ Thuật - Trường Đại Học Sư Phạm Kỹ Thuật - TP.HCM  
Địa chỉ: Phòng 601B, 1 Võ Văn Ngân, Quận Thủ Đức, Thành Phố Hồ Chí Minh. 
Điện thoại: 08-3722.1223 (8168)
Email:
tapchikhgdkt@hcmute.edu.vn

                                      
                                

Truy cập tháng: 19,972

Tổng truy cập:246,911